Strong subbandgap photoconductivity in GaP implanted withTi
Photovoltaic solar cells based on the intermediate band (IB) concept could greatly enhance theefficiency of future devices. We have analyzed the electrical and photoconductivity propertiesof GaP supersaturated with Ti to assess its suitability for IB solar cells. GaP:Ti was obtained byion implantati...
| Autores: | ; ; ; ; ; ; ; ; |
|---|---|
| Tipo de documento: | Artigo |
| Data de publicação: | 2018 |
| País: | España |
| Recursos: | Universidad Complutense de Madrid (UCM) |
| Repositório: | Docta Complutense |
| Idioma: | Inglês |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/12891 |
| Acesso em linha: | https://hdl.handle.net/20.500.14352/12891 |
| Nível de acesso: | Acesso aberto |
| Palavra-chave: | 621.382.3 gallium phosphide high efficiency intermediate band pulsed laser melting supersaturated titanium Electricidad Electrónica (Física) 2202.03 Electricidad |
| Resumo: | Photovoltaic solar cells based on the intermediate band (IB) concept could greatly enhance theefficiency of future devices. We have analyzed the electrical and photoconductivity propertiesof GaP supersaturated with Ti to assess its suitability for IB solar cells. GaP:Ti was obtained byion implantation followed by pulsed‐laser melting (PLM) using an ArF excimer laser. It was foundthat PLM energy densities between 0.35 and 0.55 J/cm2produced a good recovery of thecrystalline structure of GaP (both unimplanted and implanted with Ti), as evidenced by highmobility measured values (close to the reference GaP). Outside this energy density window,the PLM failed to recover the crystalline structure producing a low mobility layer that iselectrically isolated from the substrate. Spectral photoconductivity measurements wereperformed by using the van der Pauw set up. For GaP:Ti a significant enhancement of theconductivity was observed when illuminating the sample with photon energies below 2.26 eV,suggesting that this photoconductivity is related to the presence of Ti in a concentration highenough to form an IB within the GaP bandgap. The position of the IB was estimated to be around1.1 eV from the conduction band or the valence band of GaP, which would lead to maximumtheoretical efficiencies of 25% to 35% for a selective absorption coefficients scenario and higherfor an overlapping scenario |
|---|