Physicochemical aspects of epoxide driven nano-ZrO2 hydrogel formation: Milder kinetics for better properties
Robust and highly transparent quasi amorphous ZrO2-water-glycerol hydrogels were obtained in a mild one pot procedure, based on the 2,3-epoxy-1-propanol driven alkalinization. SAXS-based characterization of the sol-gel transition revealed that an homogeneously nucleated sol composed of 2 nm primary...
| Autores: | ; ; |
|---|---|
| Tipo de documento: | Artigo |
| Estado: | Published version |
| Data de publicação: | 2016 |
| País: | Argentina |
| Recursos: | Consejo Nacional de Investigaciones Científicas y Técnicas |
| Repositório: | CONICET Digital (CONICET) |
| Idioma: | Inglês |
| OAI Identifier: | oai:ri.conicet.gov.ar:11336/59003 |
| Acesso em linha: | http://hdl.handle.net/11336/59003 |
| Nível de acesso: | Acesso aberto |
| Palavra-chave: | Hydrogels Saxs Gelification https://purl.org/becyt/ford/1.4 https://purl.org/becyt/ford/1 |
| Resumo: | Robust and highly transparent quasi amorphous ZrO2-water-glycerol hydrogels were obtained in a mild one pot procedure, based on the 2,3-epoxy-1-propanol driven alkalinization. SAXS-based characterization of the sol-gel transition revealed that an homogeneously nucleated sol composed of 2 nm primary particles continuously grows up to a critical size of 5-6 nm, when gelation takes place. These particles reach a size of 8-10 nm, depending on the Zr(iv) concentration. Conductivity measurements offer an overall in situ assessment of the reaction rate. The gelled samples share a common trend: once the conductivity decays to 40% of the starting value, the primary particles nucleate and when this decay reaches 20%, the sol-gel transition takes place. The mild conditions employed herein prevent massive ripening and recrystallization leaving hydrogels with extremely low undesired visible light scattering. This suitable nanostructure was achieved in a wide range of total Zr(iv) concentrations or water to glycerol ratios. |
|---|